Metallizzazione delle Materie Plastiche
Plating On PlasticsPlastics
1
![Page 2: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/2.jpg)
Meterie Plastiche utilizzate
ABS – AcriloNitrile Butadiene StireneABS-PC – ABS + PolicarbonatoNylon – Poliammide, rinforzata generalmente con fibra di vetroEpossidica – TermoindurentePP – PolipropilenePP – PolipropilenePE – PolietilenePoliestere con cariche di CaCO3
AltreABS e ABS+PC rappresentano il 90% del volume
2
![Page 3: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/3.jpg)
Ciclo di massima POP
Swelling – OpzionaleMordenzatura o EtchingNeutralizzazioneCondizionamentoCatalisiAcceleranteAcceleranteNichelatura chimicaNickel strike (elettrolitico) opzionaleRame strike (per immersione) opzionaleInizio sequenza elettrolitica
3
![Page 4: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/4.jpg)
Swelling
Rapida (generalmente) immersione in una miscela acquosa di speciali solventi con caratteristiche deplastificantiSi ottiene un rigonfiamento dello strato superficiale della plastica favorendo una più corretta mordenzatura/etchingE’ in genere riservato all’ABS+PC con elevate quantità di PC (>55%), PP o NylonSe il processo viene spinto in modo eccessivo, lo strato rigonfiato stesso può essere causa di scarsa aderenza
4
![Page 5: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/5.jpg)
Mordenzatura/ Etching
Fase in cui si realizza l’intacco della superficieSi utilizza una soluzione CrO3/H2SO43 2 4
Materie plastiche più resistenti richiedono tempi e/o temperature più alti (ABS+PC)
5
![Page 6: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/6.jpg)
Mordenzatura/ Etching
Butadiene
Schema meccanismo della mordenzatura
6
AcriloNitrile Stirene
![Page 7: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/7.jpg)
Mordenzatura/ Etching
A 70°C in 7 minuti si ottiene una velocità di intacco di circa 5 mg/dm2 sull’ABSPer ogni grammo di ABS mordenzato si generano circa 6 g di Cr3+
I limiti di Cr3+ sono generalmente 15 – 35 g/l. Valori inferiori possono determinare un intacco Valori inferiori possono determinare un intacco troppo profondo, superiori un intacco insufficiente.Il Cr3+ deve essere eliminato con adeguati sistemi di rigenerazione
7
![Page 8: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/8.jpg)
Rigenerazione Cromo Trivalente
8
![Page 9: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/9.jpg)
Schema vasi porosi multipli
9
![Page 10: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/10.jpg)
Efficienza dei vasi porosi
Al 100% di efficienza 1,5 Ah convertono 1 g di Cr3+ a Cr6+
Con una concentrazione di Cr3+ > 20 g/l l’efficienza è circa 90%A 10 g/l l’efficienza scende al 50%100 m2 ora producono circa 325 g di Cr3+ per 100 m2 ora producono circa 325 g di Cr3+ per cui (1,5 Ah x 325) / 0,9 = 542 A. Ipotizzando per ogni cella con una capacità di circa 150 A occorreranno 4 celle per un corretto mantenimentoSulla base di una efficienza del 90%
10
![Page 11: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/11.jpg)
Neutralizzazione
La superficie della plastica dopo la mordenzatura, sebbene abbia subito vari lavaggi, presenta un elevata concentrazione di Cr6+ che impedisce la successiva fase di catalisi (Pd)La neutralizzazione elimina il Cr6+ consentendo il corretto adsorbimento del catalizzatore (Pd)Se da una parte si tende ad eliminare quanto più Se da una parte si tende ad eliminare quanto più possibile il Cr6+ dalla superficie dei pezzi, dall’altra è importante non eccedere nella fase di neutralizzazione in quanto il Cr6+ che resta all’interno del plastisol dei telai è responsabile della mancata metallizzazione dei telai.
11
![Page 12: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/12.jpg)
Condizionamento
Viene effettuata come passaggio immediatamente precedente la catalisi.E’ semplicemente una soluzione con una concentrazione di HCl uguale alla fase di catalisiNon essendoci gradiente di concentrazione (o Non essendoci gradiente di concentrazione (o quasi), viene favorito il rapido scambio di soluzione sulla superficiePer lo stesso motivo, aiuta a mantenere la corretta concentrazione di HCl nella catalisi
12
![Page 13: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/13.jpg)
Catalisi/Palladio
Fase in cui alla superficie viene fatto adsorbire un colloide di Pd.I nuclei di Pd saranno i siti attivi dove avrà inizio la deposizione dei nichel chimico.Le particelle costituenti il colloide hanno generalmente dimensioni 0,1 - 0,3 micron e vengono tenute in sospensione con ioni Sn (sia bivalente che tetravalente sospensione con ioni Sn (sia bivalente che tetravalente seppure molto meno efficaciemente) in condizioni di elevata acidità (HCl)Le particelle del colloide si muovono all’interno del colloide in modo “autonomo” (moto Browniano) o per effetto della movimentazione meccanica della soluzione
13
![Page 14: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/14.jpg)
Catalisi/Palladio
Ioni Sn2+ in quantità sufficiente
14
Schema di struttura corretta
![Page 15: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/15.jpg)
Catalisi/Palladio
Ioni Sn2+ in quantità insufficiente
Il colloide precipita
15
Schema di struttura non corretta
![Page 16: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/16.jpg)
Catalisi/Palladio
Poco favorevole come nucleo attivo
Molto favorevole come nucleo attivo
Superfi
Superfi
16
cie
Plastica
cie
Plastica
![Page 17: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/17.jpg)
Accelerante
Superficie
17
Plastica
![Page 18: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/18.jpg)
Accelerante
Soluzione che scioglie “selettivamente” lo stagno dalla superficieLa superficie ha generalmente una quantità di Pd e di Sn di:
Prima dell’accelerante2,8 micro gr di Pd e 5,8 micro gr di Sn per cmq2,8 micro gr di Pd e 5,8 micro gr di Sn per cmqRapporto circa 1:2Dopo l’accelerante2,3 micro gr di Pd e 2,8 micro gr di Sn per cmqRapporto circa 1:1
18
![Page 19: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/19.jpg)
Nichelatura chimica
Operazione nella quale si produce il primo rivestimento metallico al seguito del quale la superficie diventa conduttivaIl colloide di Palladio (catalisi), opportunamente impoverito di Stagno (accelerante), sulla superficie, agisce da catalizzatore della reazione (finale, la reazione in realtà passa per più stadi)Ni2+ + H2PO2
- + H2O---> Ni + H2PO3- + 2H+
19
Ipofosfito Ortofosfito Nichel metallo
![Page 20: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/20.jpg)
Nichelatura chimica
(semi)Reazioni
H2PO2- + H2O→H2PO3
- + H2
Ni2+ + H2→Ni + 2H+
2H2PO2- + H2→2H2O + 2OH- + 2P
2H+ + 2e- →H2H+ + 2e- →H2
Ni2+ + H2PO2- + H2O---> Ni + H2PO3
- + 2H+
20
![Page 21: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/21.jpg)
Nichelatura Chimica
2000 X 5000 X
21
![Page 22: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/22.jpg)
Nichelatura chimica
Generalmente si considera ottimale la copertura completa della superficie da parte del nichel chimico in un tempo di 15-30 secondi (spreading rate)In 7-10 minuti il deposito di nichel raggiunge uno spessore di 0,2-0,25 micron che può essere considerato adatto alla maggior parte delle applicazioniLa misura della resistenza sulla superficie deve essere circa 30 ohm/inch (12 ohm/cm)
22
![Page 23: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/23.jpg)
Nichelatura Flash/Strike
Viene effettuata per aumentare lo spessore iniziale del rivestimento conduttivo e migliorare il contatto elettrico sui pezzi.Si utilizza una soluzione di nichel Watt (quindi con corrente) senza additivi, salvo una certa quantità di tensioattivo per evitare puntinaturee favorire la bagnabilità della superficieLa quantità di cloruri è generalmente ridotta per evitare la prematura dissoluzione dello strato di nichel chimico
23
![Page 24: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/24.jpg)
Ramatura Strike
Attraverso l’immersione in una soluzione acida che contiene rame, si ottiene un sottile rivestimento che migliore le caratteristiche elettriche della superficie.Può essere impiegato in alternativa allo strike di nichel o come ulteriore rivestimento sul nichel strike stessoSi rivela utile in particolare su pezzi che per vari motivi possono utilizzare un numero limitato di contatti elettrici o contatti di ridotte dimensione
24
![Page 25: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/25.jpg)
Rame – Bagni acidi composizione
Componente Range Ottimale
CuSO4 180-200 g/l 190 g/l
H2SO4 60-80 g/l 65 g/l
Cl- 65-90 mg/l 70 mg/l
Additivo Livellante 0,5-1,5 ml/l 1 ml/l
25
Additivo Brillantante 0,5-1,5 ml/l 1 ml/l
Additivo Polimero 3-5 ml/l 4 ml/l
ddc catodica 1-4 A/dmq 2,5 A/dmq
Temperatura 20-30 °C 22 °C
![Page 26: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/26.jpg)
Rame – Bagni acidi
Eccellenti caratteristiche di lucentezza e livellamentoOttima efficienza (100% circa) e velocità di deposizione
26
deposizioneProducono depositi duttili anche ad elevati spessori
![Page 27: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/27.jpg)
Meccanismo del livellamento
During electrolysis, leveller is strongly adsorbed on to the high CD areas of small defects. The leveller has a “shielding” effect reducing current and slowing the plating
rate
Acid Copper
Nickel
27
Substrate
SEM - Micro section
![Page 28: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/28.jpg)
Meccanismo del livellamento
In the lower current density areas of small defects leveller adsorption is much less. This allows a more normal plating rate to be maintained
Acid Copper
Nickel
28
Substrate
SEM - Micro section
![Page 29: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/29.jpg)
Meccanismo del livellamento
Levelling results in a greater deposit thickness in the centre of defects which smoothes out the surface profile
Acid Copper
Nickel
29
Substrate
SEM - Micro section
![Page 30: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/30.jpg)
Livellamento
Test use “Larry King” scratch panels, industry standard test panels, machine manufactured giving a consistent depth profile across the
full width of the lower panel surfaceAssessment is made via Optical Microscope
A “green” light filter is used on some images to intensify resolution
30
![Page 31: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/31.jpg)
Solutions: Standard carbon treated acid copper base.Concentrations: Using mid range TDS additive concentrations
Hull Cell testing: 267ml cell, Air, 2 amp 10min electrolysis @ 25oC
Mid/Low1.5 ASD
Mid4 ASD
High10 ASD
CuMac Optima – Assessing Levelling
31
Levelling was assessed using a Vickers optical microscope at the marked test points. A green filter was used on some images to improve field definition, and
reflectanceslight water staining can be seen on some areas
![Page 32: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/32.jpg)
Livellamento
Low1.5 ASD
3.3 microns
Mid4 ASD
8.8 microns
High10 ASD
22 microns
CuMac Optima plated Larry King panel at 100x magnification
32
Unplated panel at 100x magnification
![Page 33: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/33.jpg)
Nichel semilucido
Il rivestimento deve contenere < 0,005% di ZolfoGli additivi di conseguenza non devono contenere ZolfoLo spessore di nichel semilucido costituisce da metà a due terzi dello spessore complessivo di nichel
33
nichelDeve essere un deposito duttile e avere bassi livelli di tensioni interneDeve produrre una differenza di potenziale di 100-120 mV accoppiato al rivestimento lucido
![Page 34: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/34.jpg)
Nichel semilucido composizione
Componenente Range Ottimale
NiSO4 x 6H2O 220-250 g/l 230 g/l
NiCl2 x 6H2O 40-60 g/l 50 g/l
H3BO3 40-50 g/l 45 g/l
pH 3,6-4,0 3,8
34
pH 3,6-4,0 3,8
Temperatura 52-60 °C 58 °C
Additivo Duttilizzante
8 – 12 ml/l 10 ml/l
Additivo Spendogeno
0,6 – 1,0 ml/l 0,8 ml/l
![Page 35: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/35.jpg)
Nichel semilucido Step Test
35
![Page 36: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/36.jpg)
Nichel semilucido Step Test
36
![Page 37: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/37.jpg)
Nichel – Bagni lucidi composizione
Componenente Range Ottimale
NiSO4 x 6H2O 250-300 g/l 280 g/l
NiCl2 x 6H2O 60-75 g/l 65 g/l
H3BO3 40-50 g/l 45 g/l
pH 4,2-5,0 4,8
37
Temperatura 52-60 °C 58 °C
Brillantante 2a Classe 3-6 g/l NA
Brillantante 1a Classe 10-50 mg/l NA
Duttilizzante 80-300 mg/l NA
Tensioattivo 150-300 mg/l NA
![Page 38: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/38.jpg)
Nichel microporoso
Sistemi molto simili ai bagni lucidi con un livello di additivi generalmente ridottoSpessori molto bassi, 1-2 micronLe particelle di materiale inerte, in genere talco, hanno dimensioni variabili tra 1 e 5 micron e vengono mantenute in sospensione mediante forte agitazione della soluzione (aria o sistemi Venturi).Le particelle che si depositano sulla superficie vengono inglobate (parzialmente) durante la crescita del
38
inglobate (parzialmente) durante la crescita del rivestimento.Per migliorare l’efficienza del sistema, i moderni processi impiegano additivi in grado di impartire una carica elettrica alle particelle (positiva)Lo strato deve generare una differenza di potenziale di 20 mV accoppiato al nichel lucido (più nobile)
![Page 39: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/39.jpg)
Nichel microporoso
Componenente Range Ottimale
NiSO4 x 6H2O 250-300 g/l 280 g/l
NiCl2 x 6H2O 60-75 g/l 65 g/l
H3BO3 40-50 g/l 45 g/l
pH 4,2-5,0 4,8
39
Temperatura 52-60 °C 58 °C
Brillantante 2a Classe 3-6 g/l NA
Brillantante 1a Classe 10-50 mg/l NA
Additivo particelle NA NA
Tensioattivo/disperdente 150-300 mg/l NA
![Page 40: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/40.jpg)
Nichel microporoso
PRIMA DELLA CROMATURA
40
DOPO LA CROMATURA
![Page 41: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/41.jpg)
Nichel Microporoso
Il miglior modo per eseguire la conta dei pori attivi è il test CASS o NSS, ma è piuttosto lungo e inadatto ad un controllo in tempo reale della produzione
41
Il test Dubpernell che consiste nella ramatura della superficie del provino è meno preciso, ma può essere realizzato rapidamente
![Page 42: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/42.jpg)
Nichel Satinato
Processi a batch che consentono diverse finitureImpiego molto diffuso nel settore automobilistico e sanitarioRichiedono un accurato controllo dei parametri operativi
42
operativiNecessitano di frequenti interventi di manuntenzioneComportamento simile alla nichelatura lucida per ciò che riguarda le caratteristiche protettive
![Page 43: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/43.jpg)
Nichel Satinato
Componenente Range Ottimale
NiSO4 x 6H2O 450-490 g/ 470 g/l
NiCl2 x 6H2O 30-35 g/l 30 g/l
H3BO3 40-50 g/l 40 g/l
pH 4,2-5,0 4,8
43
Temperatura 52-60 °C 58 °C
Co Brillantante A (prop.) 10-20 ml/l 15 ml/l
Co Brillantante B (prop) 10-20 ml/l 15 ml/l
Additivo Satinante 0,1-1 ml/l NA
![Page 44: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/44.jpg)
Nichel Satinato
44
![Page 45: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/45.jpg)
Varie Finiture Nichel satinato
45
![Page 46: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/46.jpg)
Nichel semilucido
Il rivestimento deve contenere < 0,005% di ZolfoGli additivi di conseguenza non devono contenere ZolfoLo spessore di nichel semilucido costituisce da metà a due terzi dello spessore complessivo di nichel
46
nichelDeve essere un deposito duttile e avere bassi livelli di tensioni interneDeve produrre una differenza di potenziale di 100-120 mV accoppiato al rivestimento lucido
![Page 47: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/47.jpg)
Nichel semilucido composizione
Componenente Range Ottimale
NiSO4 x 6H2O 220-250 g/l 230 g/l
NiCl2 x 6H2O 40-60 g/l 50 g/l
H3BO3 40-50 g/l 45 g/l
pH 3,6-4,0 3,8
47
pH 3,6-4,0 3,8
Temperatura 52-60 °C 58 °C
Additivo Duttilizzante
8 – 12 ml/l 10 ml/l
Additivo Spendogeno
0,6 – 1,0 ml/l 0,8 ml/l
![Page 48: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/48.jpg)
Nichel semilucido Step Test
48
![Page 49: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/49.jpg)
Nichel semilucido Step Test
49
![Page 50: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/50.jpg)
Nichel microporoso
Sistemi molto simili ai bagni lucidi con un livello di additivi generalmente ridottoSpessori molto bassi, 1-2 micronLe particelle di materiale inerte, in genere talco, hanno dimensioni variabili tra 1 e 5 micron e vengono mantenute in sospensione mediante forte agitazione della soluzione (aria o sistemi Venturi).Le particelle che si depositano sulla superficie vengono inglobate (parzialmente) durante la crescita del
50
inglobate (parzialmente) durante la crescita del rivestimento.Per migliorare l’efficienza del sistema, i moderni processi impiegano additivi in grado di impartire una carica elettrica alle particelle (positiva)Lo strato deve generare una differenza di potenziale di 20 mV accoppiato al nichel lucido (più nobile)
![Page 51: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/51.jpg)
Nichel microporoso
Componenente Range Ottimale
NiSO4 x 6H2O 250-300 g/l 280 g/l
NiCl2 x 6H2O 60-75 g/l 65 g/l
H3BO3 40-50 g/l 45 g/l
pH 4,2-5,0 4,8
51
Temperatura 52-60 °C 58 °C
Brillantante 2a Classe 3-6 g/l NA
Brillantante 1a Classe 10-50 mg/l NA
Additivo particelle NA NA
Tensioattivo/disperdente 150-300 mg/l NA
![Page 52: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/52.jpg)
Nichel microporoso
PRIMA DELLA CROMATURA
52
DOPO LA CROMATURA
![Page 53: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/53.jpg)
Nichel Microporoso
Il miglior modo per eseguire la conta dei pori attivi è il test CASS o NSS, ma è piuttosto lungo e inadatto ad un controllo in tempo reale della produzione
53
Il test Dubpernell che consiste nella ramatura della superficie del provino è meno preciso, ma può essere realizzato rapidamente
![Page 54: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/54.jpg)
Nichel Satinato
Processi a batch che consentono diverse finitureImpiego molto diffuso nel settore automobilistico e sanitarioRichiedono un accurato controllo dei parametri operativi
54
operativiNecessitano di frequenti interventi di manuntenzioneComportamento simile alla nichelatura lucida per ciò che riguarda le caratteristiche protettive
![Page 55: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/55.jpg)
Nichel Satinato
Componenente Range Ottimale
NiSO4 x 6H2O 450-490 g/ 470 g/l
NiCl2 x 6H2O 30-35 g/l 30 g/l
H3BO3 40-50 g/l 40 g/l
pH 4,2-5,0 4,8
55
Temperatura 52-60 °C 58 °C
Co Brillantante A (prop.) 10-20 ml/l 15 ml/l
Co Brillantante B (prop) 10-20 ml/l 15 ml/l
Additivo Satinante 0,1-1 ml/l NA
![Page 56: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/56.jpg)
Nichel Satinato
56
![Page 57: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/57.jpg)
Varie Finiture Nichel satinato
57
![Page 58: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/58.jpg)
Cromatura
Tre tipi di processiAl solfatoA catalizzatore misto, base fluoruriTriplo catalizzatore, proprietarioRidotta efficienza, circa 20% (15% bagno al
58
Ridotta efficienza, circa 20% (15% bagno al solfato)Parametri operativi ristretti, soprattutto se paragonati a processi come rame e nichel
![Page 59: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/59.jpg)
Cromatura
Rivestimento finaleOttima inalterabilità della superficieElevata durezza (fino a 600-700 Vickers)Tecnologia molto matura ed affidabileImpiega Anidride Cromica, cromo esavalente, cancerogeno
59
cancerogenoForte sviluppo di alternative attraverso sistemi a base di cromo trivalenteIn campo decorativo può essere sostituito in molte applicazione con i sistemi trivalenti
![Page 60: Metallizzazione delle Materie Plastiche - plastlab.it - Seminario V04 - 18.06.2014.pdf · Deve produrre una differenza di potenziale di 100-120 mVaccoppiato al rivestimento lucido.](https://reader031.fdocument.pub/reader031/viewer/2022021621/5c695f8409d3f27c028d0978/html5/thumbnails/60.jpg)
Cromatura Composizione
Componente Range Ottimale
CrO3 170-280 g/l 220 g/l
Catalizzatore I° SO42-
Rapporto 100:1Rapporto 200:1
60
Catalizzatore II° F- 5-30 ml/l 20 ml/l
Catalizzatore III° Prop. 5-30 ml/l 20 ml/l
Temperatura 20-38 °C 30 °C