M. Alfa Rizal D. 3110030106 Yuke Sulistyaning I. 3110030118 ...
Transcript of M. Alfa Rizal D. 3110030106 Yuke Sulistyaning I. 3110030118 ...
![Page 1: M. Alfa Rizal D. 3110030106 Yuke Sulistyaning I. 3110030118 ...](https://reader036.fdocument.pub/reader036/viewer/2022062600/5866d93f1a28aba5408b9180/html5/thumbnails/1.jpg)
Disusun Oleh:
M. Alfa Rizal D. 3110030106
Yuke Sulistyaning I. 3110030118
Dosen Pembimbing :
Dr. RIDHO BAYUAJI, ST. MT. NIP. 19730710 199802 1 001
Ir. BOEDI WIBOWO,CES NIP. 19530424 198203 1 002
TUGAS AKHIR
PROGRAM STUDI DIPLOMA III TEKNIK SIPIL
FAKULTAS TEKNIK SIPIL DAN PERENCANAAN
INSTITUT TEKNOLOGI SEPULUH NOPEMBER
2013
![Page 2: M. Alfa Rizal D. 3110030106 Yuke Sulistyaning I. 3110030118 ...](https://reader036.fdocument.pub/reader036/viewer/2022062600/5866d93f1a28aba5408b9180/html5/thumbnails/2.jpg)
Latar belakang
![Page 3: M. Alfa Rizal D. 3110030106 Yuke Sulistyaning I. 3110030118 ...](https://reader036.fdocument.pub/reader036/viewer/2022062600/5866d93f1a28aba5408b9180/html5/thumbnails/3.jpg)
![Page 4: M. Alfa Rizal D. 3110030106 Yuke Sulistyaning I. 3110030118 ...](https://reader036.fdocument.pub/reader036/viewer/2022062600/5866d93f1a28aba5408b9180/html5/thumbnails/4.jpg)
![Page 5: M. Alfa Rizal D. 3110030106 Yuke Sulistyaning I. 3110030118 ...](https://reader036.fdocument.pub/reader036/viewer/2022062600/5866d93f1a28aba5408b9180/html5/thumbnails/5.jpg)
SAMA
LEBIH TINGGI
TUJUAN
![Page 6: M. Alfa Rizal D. 3110030106 Yuke Sulistyaning I. 3110030118 ...](https://reader036.fdocument.pub/reader036/viewer/2022062600/5866d93f1a28aba5408b9180/html5/thumbnails/6.jpg)
![Page 7: M. Alfa Rizal D. 3110030106 Yuke Sulistyaning I. 3110030118 ...](https://reader036.fdocument.pub/reader036/viewer/2022062600/5866d93f1a28aba5408b9180/html5/thumbnails/7.jpg)
- Mempersiapkan Material
Pasir
Semen
PhosphoGypsum
Air
![Page 8: M. Alfa Rizal D. 3110030106 Yuke Sulistyaning I. 3110030118 ...](https://reader036.fdocument.pub/reader036/viewer/2022062600/5866d93f1a28aba5408b9180/html5/thumbnails/8.jpg)
- Mempersiapkan Material
- Pengujian Material
ASTM C556 – 89 ( Kelembapan Pasir )
ASTM C128 – 93 ( Berat Jenis Pasir )
ASTM C128 – 93 ( Air Resapan Pasir )
ASTM C29 / C 29 M – 91 ( Berat Volume Pasir )
ASTM C 117-95 (Test Kebersihan Pasir Terhadap Lumpur )
ASTM C 136-95 A (Analisa Saringan Pasir )
ASTM C168 – 2003 (Standart Mutu pozzolan)
ASTM C494 – 99 ( Admixture for Concrete)
SNI 2847 – 2002 P.s. 5,4 ( Persyaratan Air )
SII 0052 – 80 (Semen)
ASTM C618-2003 (kelas pozzolan)
![Page 9: M. Alfa Rizal D. 3110030106 Yuke Sulistyaning I. 3110030118 ...](https://reader036.fdocument.pub/reader036/viewer/2022062600/5866d93f1a28aba5408b9180/html5/thumbnails/9.jpg)
- Mempersiapkan Material
- Pengujian Material
- Hasil dan Analisa Pengujian Material Komposisi dalam senyawa oksida Berat (%)
SiO2 2,40
Fe2O3 0,07
CaO 52,39
P2O5 0,85
SO3 43,59
TiO2 0,08
CuO 0,03
SrO 0,45
Yb2O3 0,14
Pasir
PhosphoGypsum
Pozzolan Kelas C
![Page 10: M. Alfa Rizal D. 3110030106 Yuke Sulistyaning I. 3110030118 ...](https://reader036.fdocument.pub/reader036/viewer/2022062600/5866d93f1a28aba5408b9180/html5/thumbnails/10.jpg)
- Merencanakan Komposisi
PercobaanPC PG pasir Air SP
Kontrol volume
gram gram gram gram gram
I 269.51 89.84 1437.39 179.67 3.59 1980.00
II 179.67 179.67 1437.39 179.67 3.59 1980.00
III 89.84 269.51 1437.39 179.67 3.59 1980.00
komposisipasir semen PG
FAS SP% % %
I 80 15 5 0.5 0.01
II 80 10 10 0.5 0.01
III 80 5 15 0.5 0.01
![Page 11: M. Alfa Rizal D. 3110030106 Yuke Sulistyaning I. 3110030118 ...](https://reader036.fdocument.pub/reader036/viewer/2022062600/5866d93f1a28aba5408b9180/html5/thumbnails/11.jpg)
- Pembuatan Benda Uji (18 buah)
- Merencanakan Komposisi
![Page 12: M. Alfa Rizal D. 3110030106 Yuke Sulistyaning I. 3110030118 ...](https://reader036.fdocument.pub/reader036/viewer/2022062600/5866d93f1a28aba5408b9180/html5/thumbnails/12.jpg)
Suhu ruangdirendam
- Pembuatan Benda Uji (18 buah)
- Merencanakan Komposisi
- Perawatan 7 hari ( diremdam & suhu ruang)
![Page 13: M. Alfa Rizal D. 3110030106 Yuke Sulistyaning I. 3110030118 ...](https://reader036.fdocument.pub/reader036/viewer/2022062600/5866d93f1a28aba5408b9180/html5/thumbnails/13.jpg)
- Pembuatan Benda Uji (18 buah)
- Merencanakan Komposisi
- Perawatan 7 hari ( diremdam & suhu ruang)
- Pengujian Kuat Tekan
![Page 14: M. Alfa Rizal D. 3110030106 Yuke Sulistyaning I. 3110030118 ...](https://reader036.fdocument.pub/reader036/viewer/2022062600/5866d93f1a28aba5408b9180/html5/thumbnails/14.jpg)
- Hasil dan Analisa
- Pembuatan Benda Uji (18 buah)
- Merencanakan Komposisi
- Perawatan 7 hari ( diremdam & suhu ruang)
- Pengujian Kuat Tekan
![Page 15: M. Alfa Rizal D. 3110030106 Yuke Sulistyaning I. 3110030118 ...](https://reader036.fdocument.pub/reader036/viewer/2022062600/5866d93f1a28aba5408b9180/html5/thumbnails/15.jpg)
- Merencanakan Komposisi
PercobaanPC PG pasir FAS(PC+PG) SP(PC+PG)
% % % % %
PG-1 0.05 0.15 0.8 0.5 0
PG-2 0.05 0.15 0.8 0.55 0
PG-3 0.04 0.16 0.8 0.5 0
PG-4 0.04 0.16 0.8 0.55 0
PercobaanPC PG pasir Air SP
Kontrol volumegram gram gram gram gram
PG-1 270.00 810.00 4320.00 540.00 0.00 5940.00
PG-2 267.57 802.70 4281.08 588.65 0.00 5940.00
PG-3 216.00 864 4320 540 0.00 5940.00
PG-4 214.05 856.22 4281.08 588.65 0.00 5940.00
![Page 16: M. Alfa Rizal D. 3110030106 Yuke Sulistyaning I. 3110030118 ...](https://reader036.fdocument.pub/reader036/viewer/2022062600/5866d93f1a28aba5408b9180/html5/thumbnails/16.jpg)
- Perawatan 7 & 28hari (tidak direndam)
suhu ruang
- Pembuatan Benda Uji (72 buah)
- Merencanakan Komposisi
![Page 17: M. Alfa Rizal D. 3110030106 Yuke Sulistyaning I. 3110030118 ...](https://reader036.fdocument.pub/reader036/viewer/2022062600/5866d93f1a28aba5408b9180/html5/thumbnails/17.jpg)
- Hasil dan Analisa Uji Kuat Tekan 7 & 28 hari
Serta Uji Porositas 28 hari
- Perawatan 7 & 28hari (tidak direndam)
- Pembuatan Benda Uji (72 buah)
- Merencanakan Komposisi
![Page 18: M. Alfa Rizal D. 3110030106 Yuke Sulistyaning I. 3110030118 ...](https://reader036.fdocument.pub/reader036/viewer/2022062600/5866d93f1a28aba5408b9180/html5/thumbnails/18.jpg)
![Page 19: M. Alfa Rizal D. 3110030106 Yuke Sulistyaning I. 3110030118 ...](https://reader036.fdocument.pub/reader036/viewer/2022062600/5866d93f1a28aba5408b9180/html5/thumbnails/19.jpg)
16,27
7,525,38
38,29
20,16
11,82
0,00
5,00
10,00
15,00
20,00
25,00
30,00
35,00
40,00
45,00
Limbah 5% Limbah 10% Limbah 15%
direndam suhu ruang
HASIL UJI EKSPERIMEN PENDAHULUAN
• Hasil kuat tekan dengan
curing suhu ruang lebih besar
dari pada dengan curing
direndam.
• Semakin bertambah rasio
limbah terhadap semen.
Semakin rendah kuat tekan
ANALISA
• Untuk eksperimen utama
digunakan curing suhu ruang.
• Untuk (limbah 5%, semen 15%)
dan (limbah 10%, semen 10%)
hasil uji sudah memenuhi
syarat. Maka akan diteliti
lebih lanjut pada komposisi
limbah 15% dengan FAS 0,5
dan 0,55 tanpa SP.
KESIMPULAN
![Page 20: M. Alfa Rizal D. 3110030106 Yuke Sulistyaning I. 3110030118 ...](https://reader036.fdocument.pub/reader036/viewer/2022062600/5866d93f1a28aba5408b9180/html5/thumbnails/20.jpg)
7,31 6,88
12,58
7,64
PG-2 limbah 15% PG-4 limbah 16%
Komposisi FAS 0,55
kuat tekan 7 hari kuat tekan 28 hari
10,05 9,57
15,09
10,44
PG-1 limbah 15% PG-3 limbah 16%
Komposisi FAS 0,5
kuat tekan 7 hari kuat tekan 28 hari
• Kuat tekan Benda uji dengan
rasio limbah terhadap semen 3:1
selalu lebih besar daripada
benda uji dengan rasio limbah
terhadap semen 4:1
• Selalu terjadi peningkatan kuat
tekan pada umur 7 hari ke umur
28 hari pada semua komposisi.
• Terjadi peningkatan kuat tekan
dari FAS 0,55 ke FAS 0,50; baik
pada umur 7 hari maupun 28 hari.
HASIL UJI EKSPERIMEN UTAMA
ANALISA HASIL UJI KUAT TEKAN
![Page 21: M. Alfa Rizal D. 3110030106 Yuke Sulistyaning I. 3110030118 ...](https://reader036.fdocument.pub/reader036/viewer/2022062600/5866d93f1a28aba5408b9180/html5/thumbnails/21.jpg)
32,33
32,85
33,52
34,34
31,00
31,50
32,00
32,50
33,00
33,50
34,00
34,50
PG-1 FAS 0.50
limbah 15%
PG-2 FAS 0.55
limbah 15%
PG-3 FAS 0.50
limbah 16%
PG-4 FAS 0.55
limbah 16%
Uji Porosity 28 hari
HASIL UJI EKSPERIMEN UTAMA
ANALISA HASIL UJI POROSITI
• Hasil porositi total benda uji
dengan rasio limbah terhadap
semen 3:1 lebih kecil daripada
benda uji dengan rasio limbah
terhadap semen 4:1
• Terjadi peningkatan kuat tekan
dari FAS 0,50 ke FAS 0,55.
jadi porositi berbanding lurus
dengan FAS
![Page 22: M. Alfa Rizal D. 3110030106 Yuke Sulistyaning I. 3110030118 ...](https://reader036.fdocument.pub/reader036/viewer/2022062600/5866d93f1a28aba5408b9180/html5/thumbnails/22.jpg)
32,33 32,85 33,52 34,34
15,0912,58
10,447,64
PG-1 FAS 0.50
limbah 15%
PG-2 FAS 0.55
limbah 15%
PG-3 FAS 0.50
limbah 16%
PG-4 FAS 0.55
limbah 16%
Porositi 28 hari (%) kuat tekan 28 hari kg/cm2
HUBUNGAN POROSITI TOTAL DENGAN KUAT TEKAN
Hasil Porositi Total berbanding
terbalik dengan hasil kuat
tekan, hal ini ditunjukkan
semua komposisi
![Page 23: M. Alfa Rizal D. 3110030106 Yuke Sulistyaning I. 3110030118 ...](https://reader036.fdocument.pub/reader036/viewer/2022062600/5866d93f1a28aba5408b9180/html5/thumbnails/23.jpg)
Analisa sifat fisik dan kimia limbah padat Petrokimia dapat
disimpulkan menurut ASTM C618-2003 (tentang standar mutu
pozzolan) jumlah unsur senyawa SiO2, Al2O3 dan Fe2O3 sama
dengan 2,47%, yang mana lebih kecil dari standar maksimal 70%,
dan mengandung CaO 52,39%, yang mana diatas standar minimal
10%. Maka limbah padat Petrokimia yang digunakan di penelitian
ini dikategorikan pozolan kelas C.
Memakaian rasio phospogypsum terhadap semen1 : 3 dapat
menaikan kuat tekan dari umur 7 hari ke 28 hari dengan kenaikan
sebesar 5,15 kg/cm2. dan memakaian FAS 0,50 menghasilkan kuat
tekan 2,28 kg/cm2 lebih besar dari FAS 0,55.
Hasil kuat tekan maksimal mencapai 15,09 kg/cm2 menunjukkan
komposisi yang direncanakan belum menghasilkan kuat tekan
yang memenuhi standar mutu bata beton menurut SII. 0285-80,
yakni dengan minimum kuat tekan rata-rata 20 kg/cm2.
![Page 24: M. Alfa Rizal D. 3110030106 Yuke Sulistyaning I. 3110030118 ...](https://reader036.fdocument.pub/reader036/viewer/2022062600/5866d93f1a28aba5408b9180/html5/thumbnails/24.jpg)
Untuk penelitian selanjutnya disarankan menggunakan FAS
0,45 dan 0,4. Dimaksudkan untuk mengurangi ruang
kosong pada mortar sehingga kuat tekan akan naik.
Disarankan untuk penelitian selanjutnya, proses
pemadatan menggunakan metode pres / langsung
menggunakan mesin pres batako agar memperoleh hasil
kuat tekan yang lebih besar.
Disarankan untuk penelitian selanjutnya, ada treatmen
pendahuluan pada phospogypsum agar bisa
menghasilkan hasil yang baik.