OPTIMASI KOMPOSISI PEROVSKIT La0,7Sr0,3Co1-yFeyO3-δ y...
Transcript of OPTIMASI KOMPOSISI PEROVSKIT La0,7Sr0,3Co1-yFeyO3-δ y...
![Page 1: OPTIMASI KOMPOSISI PEROVSKIT La0,7Sr0,3Co1-yFeyO3-δ y 0,5repository.its.ac.id/961/2/1409201722-presentation.pdf · 2016. 12. 7. · Pendahuluan Perovskit LaCoO 3. Modifikasi . Katalis](https://reader036.fdocument.pub/reader036/viewer/2022071008/5fc637b483f31c12d37f8301/html5/thumbnails/1.jpg)
TESIS – SK 092402
OPTIMASI KOMPOSISI PEROVSKIT La0,7Sr0,3Co1-yFeyO3-δ (0,1≤ y ≤ 0,5
dengan interval 0,1) sebagai MEMBRAN RAPAT
Oleh:MOHAMMAD LISIEF HARIYANTO
1409 201 722
1
![Page 2: OPTIMASI KOMPOSISI PEROVSKIT La0,7Sr0,3Co1-yFeyO3-δ y 0,5repository.its.ac.id/961/2/1409201722-presentation.pdf · 2016. 12. 7. · Pendahuluan Perovskit LaCoO 3. Modifikasi . Katalis](https://reader036.fdocument.pub/reader036/viewer/2022071008/5fc637b483f31c12d37f8301/html5/thumbnails/2.jpg)
Pendahuluan
Perovskit LaCoO3
Modifikasi
Katalis aktif dan selektif reaksi oksidasiparsial gas metana
Perovskit La1-xSrxCo1-yFeyO3-δ (LSCF)
2
terkenal sebagai
Perovskit LSCF 6482 (Teroaka dkk., 1991) 0,6 cm3/min.cm2
contoh
Perovskit LSCF 2828 (Li dkk., 1999) 0,32 cm3/min.cm2
Perovskit LSCF 8228 (Park dkk., 2008) 0,19 mL/min.cm2
![Page 3: OPTIMASI KOMPOSISI PEROVSKIT La0,7Sr0,3Co1-yFeyO3-δ y 0,5repository.its.ac.id/961/2/1409201722-presentation.pdf · 2016. 12. 7. · Pendahuluan Perovskit LaCoO 3. Modifikasi . Katalis](https://reader036.fdocument.pub/reader036/viewer/2022071008/5fc637b483f31c12d37f8301/html5/thumbnails/3.jpg)
Permasalahan
Perovskit La0.7Sr0.3Co1-yFeyO3-δ (0.1≤y≤ 0.5)
Sifat mekanik
Kerapatan
Kekerasan
Muai panas
Konduktivitas elektrik
3
diuji
![Page 4: OPTIMASI KOMPOSISI PEROVSKIT La0,7Sr0,3Co1-yFeyO3-δ y 0,5repository.its.ac.id/961/2/1409201722-presentation.pdf · 2016. 12. 7. · Pendahuluan Perovskit LaCoO 3. Modifikasi . Katalis](https://reader036.fdocument.pub/reader036/viewer/2022071008/5fc637b483f31c12d37f8301/html5/thumbnails/4.jpg)
Metodologi Penelitian
La2O3 + SrO + Co3O4 + Fe2O3
4
La0,7Sr0,3Co1-yFeyO3-δ (0,1≤y ≤ 0,5)
La0,7Sr0,3Co0,9Fe0,1O3-δ (LSCF 7391)
0,35 La2O3 + 0,3 SrO + 0,3 Co3O4 + 0,05 Fe2O3
sebagai contoh
mencampurkan
disintesis
![Page 5: OPTIMASI KOMPOSISI PEROVSKIT La0,7Sr0,3Co1-yFeyO3-δ y 0,5repository.its.ac.id/961/2/1409201722-presentation.pdf · 2016. 12. 7. · Pendahuluan Perovskit LaCoO 3. Modifikasi . Katalis](https://reader036.fdocument.pub/reader036/viewer/2022071008/5fc637b483f31c12d37f8301/html5/thumbnails/5.jpg)
5
dipanaskan (± 75 oC)
kalsinasi (1000 oC 2 jam bertahap 3 x)
Serbuk La0,7Sr0,3Co1-yFeyO3-δ
XRD
La0,7Sr0,3Co1-yFeyO3-δ (bubur)
Padatan La0,7Sr0,3Co1-yFeyO3-δ
karakterisasi struktur
ball milling selama ± 24 jam (+ metanol)
0,35 La2O3 + 0,3 SrO + (1-y)/3 Co3O4 + y/2 Fe2O3
![Page 6: OPTIMASI KOMPOSISI PEROVSKIT La0,7Sr0,3Co1-yFeyO3-δ y 0,5repository.its.ac.id/961/2/1409201722-presentation.pdf · 2016. 12. 7. · Pendahuluan Perovskit LaCoO 3. Modifikasi . Katalis](https://reader036.fdocument.pub/reader036/viewer/2022071008/5fc637b483f31c12d37f8301/html5/thumbnails/6.jpg)
Serbuk La0,7Sr0,3Co1-yFeyO3-δ
Hidraulik Press ( 4 ton selama ± 15 menit)
Pelet (koin) tebal ± 2 mm dan diamater ± 12 mm
KarakterisasiMorfologipermukaan
Konduktivitaselektrik
Tingkatkekerasan
Muai panas
6
dilakukan
SEM
Vicker Hardness LCR meter
TMA
![Page 7: OPTIMASI KOMPOSISI PEROVSKIT La0,7Sr0,3Co1-yFeyO3-δ y 0,5repository.its.ac.id/961/2/1409201722-presentation.pdf · 2016. 12. 7. · Pendahuluan Perovskit LaCoO 3. Modifikasi . Katalis](https://reader036.fdocument.pub/reader036/viewer/2022071008/5fc637b483f31c12d37f8301/html5/thumbnails/7.jpg)
7
![Page 8: OPTIMASI KOMPOSISI PEROVSKIT La0,7Sr0,3Co1-yFeyO3-δ y 0,5repository.its.ac.id/961/2/1409201722-presentation.pdf · 2016. 12. 7. · Pendahuluan Perovskit LaCoO 3. Modifikasi . Katalis](https://reader036.fdocument.pub/reader036/viewer/2022071008/5fc637b483f31c12d37f8301/html5/thumbnails/8.jpg)
8
Difraktogram LSCF dan LaCoO3In
tens
itas (
cps)
2θ (o)
A. Sintesis LSCF
![Page 9: OPTIMASI KOMPOSISI PEROVSKIT La0,7Sr0,3Co1-yFeyO3-δ y 0,5repository.its.ac.id/961/2/1409201722-presentation.pdf · 2016. 12. 7. · Pendahuluan Perovskit LaCoO 3. Modifikasi . Katalis](https://reader036.fdocument.pub/reader036/viewer/2022071008/5fc637b483f31c12d37f8301/html5/thumbnails/9.jpg)
Difraktogram Perovskit La0,7Sr0,3Co1-yFeyO3-δ
2θ (o)
Inte
nsita
s (cp
s)
9
![Page 10: OPTIMASI KOMPOSISI PEROVSKIT La0,7Sr0,3Co1-yFeyO3-δ y 0,5repository.its.ac.id/961/2/1409201722-presentation.pdf · 2016. 12. 7. · Pendahuluan Perovskit LaCoO 3. Modifikasi . Katalis](https://reader036.fdocument.pub/reader036/viewer/2022071008/5fc637b483f31c12d37f8301/html5/thumbnails/10.jpg)
Difraktogram semua komposisi perovskit La0,7Sr0,3Co1-yFeyO3-δ
10
2θ (o)
![Page 11: OPTIMASI KOMPOSISI PEROVSKIT La0,7Sr0,3Co1-yFeyO3-δ y 0,5repository.its.ac.id/961/2/1409201722-presentation.pdf · 2016. 12. 7. · Pendahuluan Perovskit LaCoO 3. Modifikasi . Katalis](https://reader036.fdocument.pub/reader036/viewer/2022071008/5fc637b483f31c12d37f8301/html5/thumbnails/11.jpg)
Sampel 2θ (o) Intensitas (cps)
y = 0,1 33,06; 47,27 dan 58,71 787; 475 dan 446
y = 0,2 32,98; 47,39 dan 58,66 725; 451 dan 427
y = 0,3 32,78; 47,22 dan 58,59 618; 419 dan 409
y = 0,4 32,71; 47,11 dan 58,47 615; 352 dan 339
y = 0,5 32,62; 46,96 dan 58,29 610; 335 dan 324
Pengaruh substituen Fe terhadap pergeseran sudut difraksi dan intensitas puncak perovskit La0,7Sr0,3Co1-yFeyO3-δ
11
![Page 12: OPTIMASI KOMPOSISI PEROVSKIT La0,7Sr0,3Co1-yFeyO3-δ y 0,5repository.its.ac.id/961/2/1409201722-presentation.pdf · 2016. 12. 7. · Pendahuluan Perovskit LaCoO 3. Modifikasi . Katalis](https://reader036.fdocument.pub/reader036/viewer/2022071008/5fc637b483f31c12d37f8301/html5/thumbnails/12.jpg)
Pengaruh substituen Fe terhadap perubahan tebal dan perubahan diameter membran perovskit LSCF
12
B. Preparasi LSCF menjadi Membran
0,1 0,2 0,3 0,4 0,5
∆ Τe
bal (
mm)
Substituen Fe (mol)
∆ Diam
eter (
mm)
![Page 13: OPTIMASI KOMPOSISI PEROVSKIT La0,7Sr0,3Co1-yFeyO3-δ y 0,5repository.its.ac.id/961/2/1409201722-presentation.pdf · 2016. 12. 7. · Pendahuluan Perovskit LaCoO 3. Modifikasi . Katalis](https://reader036.fdocument.pub/reader036/viewer/2022071008/5fc637b483f31c12d37f8301/html5/thumbnails/13.jpg)
No. Sampel Kekerasan (Hv)
1. LSCF 7391 805,31
2. LSCF 7382 720,34
3. LSCF 7373 615,31
4. LSCF 7364 475,07
5. LSCF 7355 386,60
Tingkat Kekerasan membran LSCF
13
C. Karakteristik Membran LSCF
![Page 14: OPTIMASI KOMPOSISI PEROVSKIT La0,7Sr0,3Co1-yFeyO3-δ y 0,5repository.its.ac.id/961/2/1409201722-presentation.pdf · 2016. 12. 7. · Pendahuluan Perovskit LaCoO 3. Modifikasi . Katalis](https://reader036.fdocument.pub/reader036/viewer/2022071008/5fc637b483f31c12d37f8301/html5/thumbnails/14.jpg)
0,1 0,2 0,3 0,4 0,5
400
500
600
700
800
Ting
kat k
eker
asan
(Hv)
Komposisi Fe
By Lisief
Grafik hubungan antara komposisi Fe dengan tingkat kekerasan
14
![Page 15: OPTIMASI KOMPOSISI PEROVSKIT La0,7Sr0,3Co1-yFeyO3-δ y 0,5repository.its.ac.id/961/2/1409201722-presentation.pdf · 2016. 12. 7. · Pendahuluan Perovskit LaCoO 3. Modifikasi . Katalis](https://reader036.fdocument.pub/reader036/viewer/2022071008/5fc637b483f31c12d37f8301/html5/thumbnails/15.jpg)
LSCF 7355 LSCF 7364
LSCF 7373 LSCF 7382 LSCF 7391
Morfologi permukaan LSCF menggunakan SEM
15
![Page 16: OPTIMASI KOMPOSISI PEROVSKIT La0,7Sr0,3Co1-yFeyO3-δ y 0,5repository.its.ac.id/961/2/1409201722-presentation.pdf · 2016. 12. 7. · Pendahuluan Perovskit LaCoO 3. Modifikasi . Katalis](https://reader036.fdocument.pub/reader036/viewer/2022071008/5fc637b483f31c12d37f8301/html5/thumbnails/16.jpg)
16
Koefisien Muai Panas Rata-Rata Membran LSCF
0,1 0,2 0,3 0,4 0,510
11
12
13
14
15
16
17
Koefi
sien T
ermal
(ppm/
°C)
Substituen Fe (mol)
![Page 17: OPTIMASI KOMPOSISI PEROVSKIT La0,7Sr0,3Co1-yFeyO3-δ y 0,5repository.its.ac.id/961/2/1409201722-presentation.pdf · 2016. 12. 7. · Pendahuluan Perovskit LaCoO 3. Modifikasi . Katalis](https://reader036.fdocument.pub/reader036/viewer/2022071008/5fc637b483f31c12d37f8301/html5/thumbnails/17.jpg)
Data konduktivitas elektrik pada perovskit LSCF
17
Komposisi
Fe
Konduktivitas Membran ( S/cm)
300 oC 350 oC 400 oC 450 oC 500 oC
0,1 6,65 x10-5 7,47 x10-5 6,84 x10-5 5,9 x10-5 4,64 x10-5
0,2 10,0 x10-5 10,7 x10-5 8,54 x10-5 6,0 x10-5 6,39 x10-5
0,3 62,3 x10-5 191,4 x10-5 393,4 x10-5 368,4 x10-5 670,8 x10-5
0,4 6,33 x10-5 7,77 x10-5 11,4 x10-5 6,07 x10-5 5,93 x10-5
0,5 12,1 x10-5 8,47 x10-5 8,33 x10-5 8,41 x10-5 5,0 x10-5
![Page 18: OPTIMASI KOMPOSISI PEROVSKIT La0,7Sr0,3Co1-yFeyO3-δ y 0,5repository.its.ac.id/961/2/1409201722-presentation.pdf · 2016. 12. 7. · Pendahuluan Perovskit LaCoO 3. Modifikasi . Katalis](https://reader036.fdocument.pub/reader036/viewer/2022071008/5fc637b483f31c12d37f8301/html5/thumbnails/18.jpg)
Konduktivitas terhadap perubahan suhu
300 350 400 450 5004
6
8
10
12
Kon
dukt
ivita
s ( x
10-3
S/m
)
Suhu (°)
LSCF 7355 LSCF 7364 LSCF 7382 LSCF 7391
300 350 400 450 5000
100
200
300
400
500
600
700
Kon
dukt
ivita
s (x
10-3 S
/m)
Suhu (°C)
LSCF 7373
18
![Page 19: OPTIMASI KOMPOSISI PEROVSKIT La0,7Sr0,3Co1-yFeyO3-δ y 0,5repository.its.ac.id/961/2/1409201722-presentation.pdf · 2016. 12. 7. · Pendahuluan Perovskit LaCoO 3. Modifikasi . Katalis](https://reader036.fdocument.pub/reader036/viewer/2022071008/5fc637b483f31c12d37f8301/html5/thumbnails/19.jpg)
Kesimpulan Membran perovskit yang paling sesuai
diaplikasikan sebagai membran katalis oksidasi gas metana adalah perovskit dengan komposisi LSCF 7373
Membran perovskit LSCF 7373 memiliki kristalinitas, kerapatan, kekerasan dan konduktivitas yang tinggi serta memiliki muai panas yang rendah
Membran tersebut memiliki nilai kekerasan 615.31 Hv; konduktivitas elektrik 670.8x10-3 S/m; serta koefisien muai panas 13.98 ppm/ oC
19
![Page 20: OPTIMASI KOMPOSISI PEROVSKIT La0,7Sr0,3Co1-yFeyO3-δ y 0,5repository.its.ac.id/961/2/1409201722-presentation.pdf · 2016. 12. 7. · Pendahuluan Perovskit LaCoO 3. Modifikasi . Katalis](https://reader036.fdocument.pub/reader036/viewer/2022071008/5fc637b483f31c12d37f8301/html5/thumbnails/20.jpg)
• Disampaikan kepada:• Bapak Hamzah Fansuri, M. Si., Ph.D. (Pembimbing)• Ibu Prof. Dr. rer. nat. Irmina Kris Murwani (Penguji)• Ibu Dr. Fahimah Martak, M. Si (Penguji)• Bapak Suprapto, Ph.D. (Penguji)• Kepala Lab. Studi Energi dan Rekayasa ITS• Kepala Lab. Kimia Fisika FMIPA ITS• Kepala Lab. Kimia Anorganik FMIPA ITS• Kepala Lab. Material Fisika FMIPA ITS• Kepala Lab. Kimia Fisika FMIPA ITB
20
![Page 21: OPTIMASI KOMPOSISI PEROVSKIT La0,7Sr0,3Co1-yFeyO3-δ y 0,5repository.its.ac.id/961/2/1409201722-presentation.pdf · 2016. 12. 7. · Pendahuluan Perovskit LaCoO 3. Modifikasi . Katalis](https://reader036.fdocument.pub/reader036/viewer/2022071008/5fc637b483f31c12d37f8301/html5/thumbnails/21.jpg)
21
STOP
![Page 22: OPTIMASI KOMPOSISI PEROVSKIT La0,7Sr0,3Co1-yFeyO3-δ y 0,5repository.its.ac.id/961/2/1409201722-presentation.pdf · 2016. 12. 7. · Pendahuluan Perovskit LaCoO 3. Modifikasi . Katalis](https://reader036.fdocument.pub/reader036/viewer/2022071008/5fc637b483f31c12d37f8301/html5/thumbnails/22.jpg)
22
No.Jenis LSCF
Sebelum Sesudah
Tebal (mm)
Diameter (mm)
Tebal (mm)
Diameter (mm)
1. 7355 ± 2 ± 12 1.9 10.612. 7364 ± 2 ± 12 1.86 10.533. 7373 ± 2 ± 12 1.79 10.364. 7382 ± 2 ± 12 1.77 10.355. 7391 ± 2 ± 12 1.68 10.35
Perbandingan ukuran sampel sebelum dan sesudah disinter
![Page 23: OPTIMASI KOMPOSISI PEROVSKIT La0,7Sr0,3Co1-yFeyO3-δ y 0,5repository.its.ac.id/961/2/1409201722-presentation.pdf · 2016. 12. 7. · Pendahuluan Perovskit LaCoO 3. Modifikasi . Katalis](https://reader036.fdocument.pub/reader036/viewer/2022071008/5fc637b483f31c12d37f8301/html5/thumbnails/23.jpg)
23
Perbandingan volume membran perovskit LSCF sebelum dan sesudah disinter
Sampel LSCFVolume sebelum
disinter (mm3)
Volume sesudah
disinter (mm3)
Perubahan Volume (mm3)
7355 ± 226.29 168.05 58.24
7364 ± 226.29 162.04 64.26
7373 ± 226.29 150.95 75.36
7382 ± 226.29 148.98 77.34
7391 ± 226.29 141.40 84.93
23
![Page 24: OPTIMASI KOMPOSISI PEROVSKIT La0,7Sr0,3Co1-yFeyO3-δ y 0,5repository.its.ac.id/961/2/1409201722-presentation.pdf · 2016. 12. 7. · Pendahuluan Perovskit LaCoO 3. Modifikasi . Katalis](https://reader036.fdocument.pub/reader036/viewer/2022071008/5fc637b483f31c12d37f8301/html5/thumbnails/24.jpg)
0,1 0,2 0,3 0,4 0,50
5
10
15
20
25
30
35
40
Shrin
kage
( %
)
Substituen Fe
Pengaruh substituen Fe terhadap Shrinkage sampel perovskit LSCF
24
![Page 25: OPTIMASI KOMPOSISI PEROVSKIT La0,7Sr0,3Co1-yFeyO3-δ y 0,5repository.its.ac.id/961/2/1409201722-presentation.pdf · 2016. 12. 7. · Pendahuluan Perovskit LaCoO 3. Modifikasi . Katalis](https://reader036.fdocument.pub/reader036/viewer/2022071008/5fc637b483f31c12d37f8301/html5/thumbnails/25.jpg)
25
Sampel Rentang suhu
(°C)
Rata-rata TEC
(ppm/°C)
LSCF 7355 103 – 874 16.41
LSCF 7364 103.10 - 874.95 14.535
LSCF 7373 102 - 874.35 13.98
LSCF 7382 101.67 - 874.52 14.69
LSCF 7391 102.96 - 874.48 10.895
Nilai Koefisien Muai Panas Rata-Rata Membran PerovskitLa0.7Sr0.3Co1-yFeyO3-δ
![Page 26: OPTIMASI KOMPOSISI PEROVSKIT La0,7Sr0,3Co1-yFeyO3-δ y 0,5repository.its.ac.id/961/2/1409201722-presentation.pdf · 2016. 12. 7. · Pendahuluan Perovskit LaCoO 3. Modifikasi . Katalis](https://reader036.fdocument.pub/reader036/viewer/2022071008/5fc637b483f31c12d37f8301/html5/thumbnails/26.jpg)
100 200 300 400 500 600 700 800 900 1000 1100
0
3
5
8
10
13
15
18
20
23
25
28
Eksp
ansi
terma
l (ppm
/o C)
Suhu (oC)
LSCF 7391 LSCF 7382 LSCF 7373 LSCF 7364 LSCF 7355
By Lisief
Pengaruh perubahan suhu terhadap ekspansi termal pada membran oksida perovskit LSCF
26
![Page 27: OPTIMASI KOMPOSISI PEROVSKIT La0,7Sr0,3Co1-yFeyO3-δ y 0,5repository.its.ac.id/961/2/1409201722-presentation.pdf · 2016. 12. 7. · Pendahuluan Perovskit LaCoO 3. Modifikasi . Katalis](https://reader036.fdocument.pub/reader036/viewer/2022071008/5fc637b483f31c12d37f8301/html5/thumbnails/27.jpg)
0,00E+000 1,00E+008 2,00E+008 3,00E+008 4,00E+008 5,00E+008 6,00E+008 7,00E+008
-1,00E+008
-2,00E+008
-3,00E+008
-4,00E+008
LSCF 7355 LSCF 7364 LSCF 7373 LSCF 7382 LSCF 7391
Z" (Ω
)
Z' (Ω)
0,00E+000 2,00E+008 4,00E+008 6,00E+008 8,00E+008 1,00E+0090,00E+000
-1,00E+008
-2,00E+008
-3,00E+008
-4,00E+008
-5,00E+008
-6,00E+008
LSCF 7355 LSCF 7364 LSCF 7373 LSCF 7382 LSCF 7391
Z" (Ω
)
Z' (Ω)
0,00E+000 2,00E+008 4,00E+008 6,00E+008 8,00E+0080,00E+000
-1,00E+008
-2,00E+008
-3,00E+008
-4,00E+008
-5,00E+008
LSCF 7355 LSCF 7364 LSCF 7373 LSCF 7382 LSCF 7391
Z" (Ω
)
Z' (Ω)
0,00E+000 1,00E+008 2,00E+008 3,00E+008 4,00E+008 5,00E+008 6,00E+0080,00E+000
-5,00E+007
-1,00E+008
-1,50E+008
-2,00E+008
-2,50E+008
-3,00E+008
-3,50E+008
Z" (Ω
)
Z' (Ω)
LSCF 7355 LSCF 7364 LSCF 7373 LSCF 7382 LSCF 7391
0,00E+000 1,00E+008 2,00E+008 3,00E+008 4,00E+008 5,00E+008 6,00E+0080,00E+000
-5,00E+007
-1,00E+008
-1,50E+008
-2,00E+008
-2,50E+008
-3,00E+008
Z" (Ω
)
Z'(Ω)
LSCF 7355 LSCF 7364 LSCF 7373 LSCF 7382 LSCF 7391
300oC 350oC
400oC 450oC
500oC
27
Spektra impedansi dari LSCF