HIGH THROUGHPUT MICROSTRUCTURE-MECHANICAL PROPERTY DATA COLLECTIONAli Khosravani, Jordan Weaver, Saikiranmayee Samudrala, Surya R. Kalidindi
EBSD scan of 1,824,372 data points with 4 μm spatial resolution---- 12 hours
Time and Cost in Microstructure Characterization , such as EBSD scan
1 mm
High resolution data collection at Grain Boundary regionsLow resolution scan pattern400 scan pointsScan time (90 fps) : 4.5 sec
High resolution adaptive scan pattern2,600 scan pointsScan time (90 fps) : 29 sec
High resolution scan pattern102,400 scan pointsScan time (90 fps) : 19 min
Georgia Instituteof Technology
Nanoindentation Arm
1
2
Distance from the Boundary (µm)
21
The George W. Woodruff School of mechanical Engineering, Georgia Institute of Technology, Atlanta GA
1µm
10µm
100µm
1000+µm
Nanoindentation Micro Macro
MULTISCALE MECHANICAL TEST METHOD
EBSD detector
Sample
Indenter tip
SEM pole piece
Kernel average misorientation (KAM)
Step 6 Step 1Step 2Step 3Step 4Step 5
1
2
4
3
5
6
Does the microstructure of the selected sample represent the microstructure of entire part?
Higher resolution & smaller area vs. Lower resolution & larger area
• BSE image collection is faster than EBSD data collection
• BSE image can be used to locate the coordinates of interesting object such as grain boundaries
Quench Rate Gradient
FurnaceConstant RT
A set of thermocouples
Thermo-Mechanical Gradient Processes
Double Cone Compression
Sample
Total Strain Gradient from DICDistance
Tem
pera
ture
A set of thermocouples
Distance
Cool
ing
rate
Aging Temperature Gradient
Martensite Laths Ferrite Grains
IN-SITU NANOINDENTATION TEST INTEGRATED NANOINDENTATION WITH SMART EBSD
How many samples are required and how many tests have to be performed to get true measurements of mechanical properties for a given microstructure?
50 μm
Connection of the mechanical response of a large sample with the microstructure of a small area