1 Introduction to Forming Roughly into following categories: Dry pressing; die pressing, isostatic...
-
Upload
kenneth-houston -
Category
Documents
-
view
231 -
download
0
Transcript of 1 Introduction to Forming Roughly into following categories: Dry pressing; die pressing, isostatic...
![Page 1: 1 Introduction to Forming Roughly into following categories: Dry pressing; die pressing, isostatic pressing, hot pressing Extrusion Injection molding.](https://reader035.fdocument.pub/reader035/viewer/2022062314/56649eac5503460f94bb211d/html5/thumbnails/1.jpg)
1
Introduction to Forming
Roughly into following categories:Dry pressing; die pressing, isostatic
pressing, hot pressingExtrusion Injection moldingCasting: slip casting, tape casting, gel
castingFactors to be considered: complexity of object, size, quantity (production rate) etc.
Che5700 陶瓷粉末處理
![Page 2: 1 Introduction to Forming Roughly into following categories: Dry pressing; die pressing, isostatic pressing, hot pressing Extrusion Injection molding.](https://reader035.fdocument.pub/reader035/viewer/2022062314/56649eac5503460f94bb211d/html5/thumbnails/2.jpg)
2Taken from TA Ring, 1996
![Page 3: 1 Introduction to Forming Roughly into following categories: Dry pressing; die pressing, isostatic pressing, hot pressing Extrusion Injection molding.](https://reader035.fdocument.pub/reader035/viewer/2022062314/56649eac5503460f94bb211d/html5/thumbnails/3.jpg)
3
Processing Aids
For different forming techniques, the additives may be different; e.g. in the following table, the molecular weight is not the same different viscosity, yield strength etc.
Che5700 陶瓷粉末處理
![Page 4: 1 Introduction to Forming Roughly into following categories: Dry pressing; die pressing, isostatic pressing, hot pressing Extrusion Injection molding.](https://reader035.fdocument.pub/reader035/viewer/2022062314/56649eac5503460f94bb211d/html5/thumbnails/4.jpg)
4
Comparison of system characteristics
Solvent content not same for different techniques; corresponding packing fraction and its changes also different, large change significant contraction; contraction occurs at some stage; forming, drying, or sintering; Vo =volume of organics in green body
Che5700 陶瓷粉末處理
![Page 5: 1 Introduction to Forming Roughly into following categories: Dry pressing; die pressing, isostatic pressing, hot pressing Extrusion Injection molding.](https://reader035.fdocument.pub/reader035/viewer/2022062314/56649eac5503460f94bb211d/html5/thumbnails/5.jpg)
5
Stress during forming
Che5700 陶瓷粉末處理
![Page 6: 1 Introduction to Forming Roughly into following categories: Dry pressing; die pressing, isostatic pressing, hot pressing Extrusion Injection molding.](https://reader035.fdocument.pub/reader035/viewer/2022062314/56649eac5503460f94bb211d/html5/thumbnails/6.jpg)
6
Strength of green body
If requires machining on green body (e.g. shape modification), hence need strength of green body, if not enough strength, easy to appear cracks, as following table, taken from JS Reed, 1995
Che5700 陶瓷粉末處理
![Page 7: 1 Introduction to Forming Roughly into following categories: Dry pressing; die pressing, isostatic pressing, hot pressing Extrusion Injection molding.](https://reader035.fdocument.pub/reader035/viewer/2022062314/56649eac5503460f94bb211d/html5/thumbnails/7.jpg)
7
![Page 8: 1 Introduction to Forming Roughly into following categories: Dry pressing; die pressing, isostatic pressing, hot pressing Extrusion Injection molding.](https://reader035.fdocument.pub/reader035/viewer/2022062314/56649eac5503460f94bb211d/html5/thumbnails/8.jpg)
8
General considerations
Both technical and economic factors should be considered
For advanced ceramics, microstructure control is a critical issue
Process window reflects the easiness of control; (reliability, reproducibility issue)
Cost ~ 1/ yield
There are often more than one process to choose for a specific ceramic product. meaning comparison of various factors
Che5700 陶瓷粉末處理
![Page 9: 1 Introduction to Forming Roughly into following categories: Dry pressing; die pressing, isostatic pressing, hot pressing Extrusion Injection molding.](https://reader035.fdocument.pub/reader035/viewer/2022062314/56649eac5503460f94bb211d/html5/thumbnails/9.jpg)
9
Process Window
Che5700 陶瓷粉末處理
![Page 10: 1 Introduction to Forming Roughly into following categories: Dry pressing; die pressing, isostatic pressing, hot pressing Extrusion Injection molding.](https://reader035.fdocument.pub/reader035/viewer/2022062314/56649eac5503460f94bb211d/html5/thumbnails/10.jpg)
10
Dimensional Control
Tight control of dimension superior control of process through forming and sintering plus final machining (polishing) – an expensive step
Total volume shrinkage = (drying stage) + (calcination stage) + (sintering stage) ….. Precise control depends on the control at this three stagesDry pressed, injection molded drying stage shrinkage ~ 0; extruded and slip casted parts drying stage shrinkage ~ 3-12%
Shrinkage during calcination: high for injection molding and tape casting
Che5700 陶瓷粉末處理
![Page 11: 1 Introduction to Forming Roughly into following categories: Dry pressing; die pressing, isostatic pressing, hot pressing Extrusion Injection molding.](https://reader035.fdocument.pub/reader035/viewer/2022062314/56649eac5503460f94bb211d/html5/thumbnails/11.jpg)
11
Shrinkage may not be isotropic!
Che5700 陶瓷粉末處理
![Page 12: 1 Introduction to Forming Roughly into following categories: Dry pressing; die pressing, isostatic pressing, hot pressing Extrusion Injection molding.](https://reader035.fdocument.pub/reader035/viewer/2022062314/56649eac5503460f94bb211d/html5/thumbnails/12.jpg)
12
Shaping method on grain size dependence of strength
• Source: J. Euro. Cer. Soc., 16, 1189-1200, 1996.• Methods tested: uniaxial pressing, cold isostatic pressing, pressure filtration, gel casting, and combinations; • High strength: high purity material for high fracture toughness; small size of critical flaw at instability (crack growth); grain size & flaw size both important• Any microstructure which reduce subcritical crack growth is helpful to strength
![Page 13: 1 Introduction to Forming Roughly into following categories: Dry pressing; die pressing, isostatic pressing, hot pressing Extrusion Injection molding.](https://reader035.fdocument.pub/reader035/viewer/2022062314/56649eac5503460f94bb211d/html5/thumbnails/13.jpg)
13
Experimental results from this work,showing effects of shaping methods
• Different fabrication technique – different flaw size & distributions• Gelcasting: gel formation – acrylamide + N,N’-methylene bis-acrylamide (use ammonium persulfate as initiator) + alumin powder (need several hours to complete polymerization) (final step: CIP before sintering
![Page 14: 1 Introduction to Forming Roughly into following categories: Dry pressing; die pressing, isostatic pressing, hot pressing Extrusion Injection molding.](https://reader035.fdocument.pub/reader035/viewer/2022062314/56649eac5503460f94bb211d/html5/thumbnails/14.jpg)
14
• Some techniques applied: (e.g.) ultrasonic dispersion + vacuum de-gassing of slurry + uniaxial pressing + cold isostatic pressing• Ultrasonic dispersion + pressure filtration + slow drying: to get samples with low flaw density; or pressure filtration + CIP;• Different processing techniques achieve packing homogeneity low sintering temperature to achieve high density• Casting and pressure filtration: may give rise to “cooperative alignment” of particles hence good results
![Page 15: 1 Introduction to Forming Roughly into following categories: Dry pressing; die pressing, isostatic pressing, hot pressing Extrusion Injection molding.](https://reader035.fdocument.pub/reader035/viewer/2022062314/56649eac5503460f94bb211d/html5/thumbnails/15.jpg)
15
•Batch 1, 2, 3: from gelcasting• General trend: increasing strength with decreasing grain size•
![Page 16: 1 Introduction to Forming Roughly into following categories: Dry pressing; die pressing, isostatic pressing, hot pressing Extrusion Injection molding.](https://reader035.fdocument.pub/reader035/viewer/2022062314/56649eac5503460f94bb211d/html5/thumbnails/16.jpg)
16
• 1 – 8: ranking of strength• obvious relation between strength and subcritical crack growth (flaw density or distribution – strongly related to forming techniques)
![Page 17: 1 Introduction to Forming Roughly into following categories: Dry pressing; die pressing, isostatic pressing, hot pressing Extrusion Injection molding.](https://reader035.fdocument.pub/reader035/viewer/2022062314/56649eac5503460f94bb211d/html5/thumbnails/17.jpg)
17
Lightest Object in 2002
Aerogel density as low as 0.003 g/cc (air density around 0.0014 g/cc) by NASA(source: 2002 Time Magazine)